Síntesis y caracterización de nanopartículas bimetálicas de ZNO: CU y AG por método sol gel

Se crearon diferentes proporciones de peso de nanopartículas de ZnO dopadas y no dopadas con Cu-plata. Mediante el uso de XRD, FTIR, espectroscopía UV-visible, FESEM y EDS se determinó la presencia de nanopartículas en el sol-gel (ZnO) y (ZnO:Ag). y Cu), la tarjeta estándar JCPDS para Zn (01-080-007...

Full description

Bibliographic Details
Main Authors:	Mohammed, H. Amer, Mohammed, M. Jasim, Ayesh, H. Ammar
Format:	Online
Language:	eng
Published:	Universidad Nacional de Ingeniería (UNI) en Managua 2023
Online Access:	https://www.camjol.info/index.php/NEXO/article/view/17466

id	NEXO17466
record_format	ojs
institution	Universidad Nacional de Ingeniería
collection	Nexo Revista Científica
language	eng
format	Online
author	Mohammed, H. Amer Mohammed, M. Jasim Ayesh, H. Ammar
spellingShingle	Mohammed, H. Amer Mohammed, M. Jasim Ayesh, H. Ammar Síntesis y caracterización de nanopartículas bimetálicas de ZNO: CU y AG por método sol gel
author_facet	Mohammed, H. Amer Mohammed, M. Jasim Ayesh, H. Ammar
author_sort	Mohammed, H. Amer
description	Se crearon diferentes proporciones de peso de nanopartículas de ZnO dopadas y no dopadas con Cu-plata. Mediante el uso de XRD, FTIR, espectroscopía UV-visible, FESEM y EDS se determinó la presencia de nanopartículas en el sol-gel (ZnO) y (ZnO:Ag). y Cu), la tarjeta estándar JCPDS para Zn (01-080-0074) validó la estructura hexagonal del ZnO mediante difracción de rayos X para (ZnO) y (ZnO:Ag y Cu). Calculamos el tamaño promedio de los cristales de todas las muestras producidas y observamos que el tamaño del cristal crece a medida que aumenta la proporción de dopaje de cobre y plata. Según los datos FTIR, la expansión O-H es responsable de la banda de absorción distintiva esperada en las proximidades de (3090-3665 cm-). Debido a que el KBr absorbe rápidamente CO, es posible que los picos en el rango (1550-1630 cm-1) sean causados por el KBr utilizado. Estos picos están relacionados con las vibraciones de estiramiento de C=O que son simétricas y asimétricas. La vibración de estiramiento del enlace ZnO se puede observar en forma de un pico prominente en el rango (350-780 cm). Cuando se introducen Ag y Cu en las muestras de ZnO dopadas, la fuerza máxima disminuye, lo que indica el inicio de grupos de Ag y Cu en la superficie de las nanopartículas de ZnO. La posición del enlace se desplazó como resultado de la alteración en la longitud del enlace provocada por la sustitución de iones Ag+ en los sitios de la red de ZnO. Según las mediciones UV-VIS, el ZnO puro tiene un pico a 370 nm que se vuelve rojo a 569 nm. Con concentraciones crecientes de Ag y Cu, los nanocompuestos muestran una alta absorción en la región visible porque los picos cambian monótonamente a longitude de onda más largas y hacen que el valor de la brecha de energía disminuya en 3, 2,958, 2,76, 2,74, 2,69 y 2,5 eV, respectivamente. Según los datos de la FESEM de IMAGE J, las nanopartículas tienen forma esférica o casi esférica. En los datos del EDS se pueden ver elementos Zn, Ag y Cu.
title	Síntesis y caracterización de nanopartículas bimetálicas de ZNO: CU y AG por método sol gel
title_short	Síntesis y caracterización de nanopartículas bimetálicas de ZNO: CU y AG por método sol gel
title_full	Síntesis y caracterización de nanopartículas bimetálicas de ZNO: CU y AG por método sol gel
title_fullStr	Síntesis y caracterización de nanopartículas bimetálicas de ZNO: CU y AG por método sol gel
title_full_unstemmed	Síntesis y caracterización de nanopartículas bimetálicas de ZNO: CU y AG por método sol gel
title_sort	síntesis y caracterización de nanopartículas bimetálicas de zno: cu y ag por método sol gel
title_alt	Synthesis and characterization of ZNO: CU and AG bimetallics nanoparticles by sol gel method
publisher	Universidad Nacional de Ingeniería (UNI) en Managua
publishDate	2023
url	https://www.camjol.info/index.php/NEXO/article/view/17466
work_keys_str_mv	AT mohammedhamer synthesisandcharacterizationofznocuandagbimetallicsnanoparticlesbysolgelmethod AT mohammedmjasim synthesisandcharacterizationofznocuandagbimetallicsnanoparticlesbysolgelmethod AT ayeshhammar synthesisandcharacterizationofznocuandagbimetallicsnanoparticlesbysolgelmethod AT mohammedhamer sintesisycaracterizaciondenanoparticulasbimetalicasdeznocuyagpormetodosolgel AT mohammedmjasim sintesisycaracterizaciondenanoparticulasbimetalicasdeznocuyagpormetodosolgel AT ayeshhammar sintesisycaracterizaciondenanoparticulasbimetalicasdeznocuyagpormetodosolgel
_version_	1805399712405127168
spelling	NEXO174662024-04-01T17:20:11Z Synthesis and characterization of ZNO: CU and AG bimetallics nanoparticles by sol gel method Síntesis y caracterización de nanopartículas bimetálicas de ZNO: CU y AG por método sol gel Mohammed, H. Amer Mohammed, M. Jasim Ayesh, H. Ammar Cu-Ag doped ZnO Sol-gel Bimetallic Nanoparticals ZnO dopado con Cu-Ag sol-gel Bimetálico Nanopartículas Different weight ratios of Cu-silver-doped and non-doped ZnO nanoparticles were created, By using XRD, FTIR, UV-visible spectroscopy, FESEM, and EDS the presence of nanoparticles in the sol-gel (ZnO) and (ZnO: Ag and Cu) techniques was confirmed, the JCPDS standard card for Zn (01-080-0074) validated the hexagonal ZnO structure by X-ray diffraction for (ZnO) and (ZnO:Ag and Cu). we calculated the average crystal size of all the produced samples, and we observe that the crystal size grows as the ratio of copper and silver doping rises. According to the FTIR data, O-H expansion is responsible for the expected distinctive absorption band in the vicinity of (3090-3665 cm). Because KBr quickly absorbs CO, it is possible that the peaks in the range (1550-1630 cm) are caused by the KBr utilized. These peaks are related to the stretching vibrations of C=O that are symmetric and asymmetric. The stretching vibration of the ZnO bond can be seen in the form of a prominent peak in the (350–780 cm) range. When Ag and Cu are entered to the doped ZnO samples, the peak strength declines, indicating the start of Ag and Cu clusters on the surface of ZnO nanoparticles. The bond position was shifted as a result of alteration in bond length brought about by the substitution of Ag+ ions at the ZnO lattice sites. According to the UV-VIS measurements, pure ZnO has a peak at 370 nm that becomes red at 569 nm. With increasing concentrations of Ag and Cu, the nanocomposites show high absorption in the visible region because the peaks shift monotonously to longer wavelengths and cause the energy gap value to decrease by 3, 2.958, 2.76, 2.74, 2.69, and 2.5 eV, respectively. According to the FESEM data from IMAGE J, the nanoparticles have a spherical or nearly spherical form. Zn, Ag, and Cu elements may be seen in the EDS data. Se crearon diferentes proporciones de peso de nanopartículas de ZnO dopadas y no dopadas con Cu-plata. Mediante el uso de XRD, FTIR, espectroscopía UV-visible, FESEM y EDS se determinó la presencia de nanopartículas en el sol-gel (ZnO) y (ZnO:Ag). y Cu), la tarjeta estándar JCPDS para Zn (01-080-0074) validó la estructura hexagonal del ZnO mediante difracción de rayos X para (ZnO) y (ZnO:Ag y Cu). Calculamos el tamaño promedio de los cristales de todas las muestras producidas y observamos que el tamaño del cristal crece a medida que aumenta la proporción de dopaje de cobre y plata. Según los datos FTIR, la expansión O-H es responsable de la banda de absorción distintiva esperada en las proximidades de (3090-3665 cm-). Debido a que el KBr absorbe rápidamente CO, es posible que los picos en el rango (1550-1630 cm-1) sean causados por el KBr utilizado. Estos picos están relacionados con las vibraciones de estiramiento de C=O que son simétricas y asimétricas. La vibración de estiramiento del enlace ZnO se puede observar en forma de un pico prominente en el rango (350-780 cm). Cuando se introducen Ag y Cu en las muestras de ZnO dopadas, la fuerza máxima disminuye, lo que indica el inicio de grupos de Ag y Cu en la superficie de las nanopartículas de ZnO. La posición del enlace se desplazó como resultado de la alteración en la longitud del enlace provocada por la sustitución de iones Ag+ en los sitios de la red de ZnO. Según las mediciones UV-VIS, el ZnO puro tiene un pico a 370 nm que se vuelve rojo a 569 nm. Con concentraciones crecientes de Ag y Cu, los nanocompuestos muestran una alta absorción en la región visible porque los picos cambian monótonamente a longitude de onda más largas y hacen que el valor de la brecha de energía disminuya en 3, 2,958, 2,76, 2,74, 2,69 y 2,5 eV, respectivamente. Según los datos de la FESEM de IMAGE J, las nanopartículas tienen forma esférica o casi esférica. En los datos del EDS se pueden ver elementos Zn, Ag y Cu. Universidad Nacional de Ingeniería (UNI) en Managua 2023-12-31 info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion Peer-Reviewed Article Artículo revisado por pares application/pdf https://www.camjol.info/index.php/NEXO/article/view/17466 10.5377/nexo.v36i06.17466 Nexo Scientific Journal; Vol. 36 No. 06 (2023); 1087-1102 Nexo Revista Científica; Vol. 36 Núm. 06 (2023); 1087-1102 1995-9516 1818-6742 eng https://www.camjol.info/index.php/NEXO/article/view/17466/21428 https://creativecommons.org/licenses/by-nc-nd/4.0/

Síntesis y caracterización de nanopartículas bimetálicas de ZNO: CU y AG por método sol gel

Similar Items