Color Change of Different Dual-Cure Resin Cements After Thermocycling

El propósito de este estudio es evaluar el efecto del termociclaje en el cambio de color de los cementos de resina de doble curado sin aminas. Los bloques IPS e.max CAD se cortaron en muestras de 1 mm de espesor (N=28) y se cementaron con uno de los 4 diferentes cementos de resina de curado doble li...

Descripción completa

Detalles Bibliográficos
Autores principales:	Atay DDS, PhD, Ayşe, Palazli DDS, Zülal, Gürdal DDS, Işıl, Üşümez DDS, PhD, Aslıhan
Formato:	Online
Idioma:	eng
Publicado:	Universidad de Costa Rica 2019
Acceso en línea:	https://revistas.ucr.ac.cr/index.php/Odontos/article/view/36783

id	ODONTOS36783
record_format	ojs
institution	Universidad de Costa Rica
collection	Odovtos International Journal of Dental Sciences
language	eng
format	Online
author	Atay DDS, PhD, Ayşe Palazli DDS, Zülal Gürdal DDS, Işıl Üşümez DDS, PhD, Aslıhan
spellingShingle	Atay DDS, PhD, Ayşe Palazli DDS, Zülal Gürdal DDS, Işıl Üşümez DDS, PhD, Aslıhan Color Change of Different Dual-Cure Resin Cements After Thermocycling
author_facet	Atay DDS, PhD, Ayşe Palazli DDS, Zülal Gürdal DDS, Işıl Üşümez DDS, PhD, Aslıhan
author_sort	Atay DDS, PhD, Ayşe
description	El propósito de este estudio es evaluar el efecto del termociclaje en el cambio de color de los cementos de resina de doble curado sin aminas. Los bloques IPS e.max CAD se cortaron en muestras de 1 mm de espesor (N=28) y se cementaron con uno de los 4 diferentes cementos de resina de curado doble libres de aminas (NX3 Nexus [NX], Kerr Dental; Variolink Esthetic DC [VE], Ivoclar Vivadent; Panavia V5 [PV], Kuraray Dental; G-CEM Linkforce [GC], GC Corporation) (n=7). Se usó un espectrofotómetro para las mediciones de color. Las muestras se sometieron a termociclaje (5°C y 55°C; 5000 y 10000 ciclos). La normalidad de la distribución de datos se probó utilizando la prueba de Kolmogorov-Smirnov. El análisis estadístico se realizó mediante un análisis de varianza de dos vías (ANOVA) y las pruebas de comparación múltiple de Tukey a un nivel de significación de p<0.05. Los valores de ∆E fueron significativamente influenciados por los cementos de resina y los períodos de ciclo (p<0.05). No hubo diferencias significativas entre los grupos NX y VE después de 5000 termociclos, sin embargo, después de 10000, el grupo VE mostró valores  ∆E1 mayores que el grupo NX (p>0.05). No hubo diferencias estadísticamente significativas entre los valoresn∆E0 y ∆E1 del grupo GC, no obstante, los otros grupos se vieron afectados después de 10000 termociclos (p>0.05). Cementos de resina libres de aminas. utilizados para la cementación mostró cambio de color después del termociclaje, excepto el grupo GC. Todos los cementos de resina mostraron un cambio de color clínicamente aceptable después del termociclaje (∆E<3.5).
title	Color Change of Different Dual-Cure Resin Cements After Thermocycling
title_short	Color Change of Different Dual-Cure Resin Cements After Thermocycling
title_full	Color Change of Different Dual-Cure Resin Cements After Thermocycling
title_fullStr	Color Change of Different Dual-Cure Resin Cements After Thermocycling
title_full_unstemmed	Color Change of Different Dual-Cure Resin Cements After Thermocycling
title_sort	color change of different dual-cure resin cements after thermocycling
publisher	Universidad de Costa Rica
publishDate	2019
url	https://revistas.ucr.ac.cr/index.php/Odontos/article/view/36783
work_keys_str_mv	AT atayddsphdayse colorchangeofdifferentdualcureresincementsafterthermocycling AT palazliddszulal colorchangeofdifferentdualcureresincementsafterthermocycling AT gurdalddsisıl colorchangeofdifferentdualcureresincementsafterthermocycling AT usumezddsphdaslıhan colorchangeofdifferentdualcureresincementsafterthermocycling
_version_	1810113432382341120
spelling	ODONTOS367832021-06-09T22:02:34Z Color Change of Different Dual-Cure Resin Cements After Thermocycling Atay DDS, PhD, Ayşe Palazli DDS, Zülal Gürdal DDS, Işıl Üşümez DDS, PhD, Aslıhan Resin cements; Prosthesis Coloring; Aging Cementos de resina; Prótesis para colorear; Envejecimiento The purpose of this study is to evaluate the effect of thermocycling on the color change of the amine-free dual-cure resin cements. IPS e.max CAD blocs were cut into specimens of 1 mm thickness (N=28) and cemented with one of the 4 different amine-free dual-cure resin cements (NX3 Nexus [NX], Kerr Dental; Variolink Esthetic DC [VE], Ivoclar Vivadent; Panavia V5 [PV], Kuraray Dental; G-CEM Linkforce [GC], GC Corporation) (n=7). A spectrophotometer was used for color measurements. Specimens were subjected to thermocycling (5°C and 55°C; 5000 and 10000 cycles). Normality of data distribution was tested by using the Kolmogorov-Smirnov test. Statistical analysis was performed using a two-way analysis of variance (ANOVA) and Tukey’s multiple comparison tests at a significance level of p<0.05. ∆E values were significantly influenced by the resin cements and the cycle periods (p<0.05). There were no significant differences between NX and VE groups after 5000 thermocycling, however after 10000 thermocycling VE group showed higher ∆E1 values than NX group (p>0.05).  There were no statistically significant differences between the ∆E0 and ∆E1 values of the GC group, however the other groups were affected after 10000 thermocycling (p>0.05). Amine-free resin cements used for cementation showed color change after thermocycling except GC group. All resin cements were showed clinically acceptable color change after thermocycling (∆E < 3.5). El propósito de este estudio es evaluar el efecto del termociclaje en el cambio de color de los cementos de resina de doble curado sin aminas. Los bloques IPS e.max CAD se cortaron en muestras de 1 mm de espesor (N=28) y se cementaron con uno de los 4 diferentes cementos de resina de curado doble libres de aminas (NX3 Nexus [NX], Kerr Dental; Variolink Esthetic DC [VE], Ivoclar Vivadent; Panavia V5 [PV], Kuraray Dental; G-CEM Linkforce [GC], GC Corporation) (n=7). Se usó un espectrofotómetro para las mediciones de color. Las muestras se sometieron a termociclaje (5°C y 55°C; 5000 y 10000 ciclos). La normalidad de la distribución de datos se probó utilizando la prueba de Kolmogorov-Smirnov. El análisis estadístico se realizó mediante un análisis de varianza de dos vías (ANOVA) y las pruebas de comparación múltiple de Tukey a un nivel de significación de p<0.05. Los valores de ∆E fueron significativamente influenciados por los cementos de resina y los períodos de ciclo (p<0.05). No hubo diferencias significativas entre los grupos NX y VE después de 5000 termociclos, sin embargo, después de 10000, el grupo VE mostró valores  ∆E1 mayores que el grupo NX (p>0.05). No hubo diferencias estadísticamente significativas entre los valoresn∆E0 y ∆E1 del grupo GC, no obstante, los otros grupos se vieron afectados después de 10000 termociclos (p>0.05). Cementos de resina libres de aminas. utilizados para la cementación mostró cambio de color después del termociclaje, excepto el grupo GC. Todos los cementos de resina mostraron un cambio de color clínicamente aceptable después del termociclaje (∆E<3.5). Universidad de Costa Rica 2019-03-29 info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion Article application/pdf text/html application/epub+zip https://revistas.ucr.ac.cr/index.php/Odontos/article/view/36783 10.15517/ijds.v21i2.36783 Odovtos - International Journal of Dental Sciences; Vol. 21 No. 2 (2019): Odovtos International Journal of Dental Sciences; 53-62 Odovtos International Journal of Dental Sciences; Vol. 21 Núm. 2 (2019): Odovtos International Journal of Dental Sciences; 53-62 2215-3411 1659-1046 10.15517/ijds.v21i2 eng https://revistas.ucr.ac.cr/index.php/Odontos/article/view/36783/37399 https://revistas.ucr.ac.cr/index.php/Odontos/article/view/36783/37552 https://revistas.ucr.ac.cr/index.php/Odontos/article/view/36783/37985

Color Change of Different Dual-Cure Resin Cements After Thermocycling

Ejemplares similares